Post by Bradleee42 on Feb 18, 2011 4:41:10 GMT
Ok so this isnt a review, I today Just recieved my KC26III and after looking at the blade, the hamon dips, twice, matching up on each side. It looks almost as if at some point the steel was crimped and then re-flattened out. And on one side, its like the steel takes a dip, almost like a heart monitor. Then comes straight back up. Is this a tempernig problem that needs to be returned or is this ok? ( I'm guts telling me not OK.) Would this cause catastrophic failure in the blade, death , dimemberment, cities to crumble, "all hope lost" kind of thing? Or is this not going to effect the Overall well being of the blade. Pics of said problem. Any ideas, suggestions, or flat out advise would be most welcome. -B
|
|
|
Post by Bradleee42 on Feb 18, 2011 15:29:31 GMT
Seriously, not one reply ?
|
|
ghost
Member
Posts: 1,331
|
Post by ghost on Feb 20, 2011 6:25:20 GMT
Hmm, it looks like it rolls right off completely. Mind zooming out a bit so we can tell how close it is to the tsuba? It will not be a problem if you never cut in that region, especially close to the tsuba. It could be possible that you are only seeing the first wavelike activity of the hamon (my KC29III has 2; 1 thin one about 3-4 mm thick then a super fat 1 cm) Frank's 26 looks like it has multiple. It doesn't look like you etched it...but I wouldn't risk not being able to return it.
Send it back - just in case - unless you can spot it from a different angle. Aesthetically, a drop-off is just not cool.
|
|
|
Post by Bradleee42 on Feb 20, 2011 16:06:28 GMT
This is after the etch, I had talked to Cecil on friday and he said it wasnt structural...but I dunno.... If I can get a few opinions, I may end up sending it back.
|
|